Strategic Study of CAE >> 2003, Volume 5, Issue 7

The Theorem of the Resistance of Hydraulic Machine's Materials to Cavitation Erosion and Abrasion

Scientific and Technological University of Kunming, Kunming 650051, China

Received: 2003-02-24 Available online: 2003-07-20

Next Previous

Abstract

In order to confirm the dependence of the resistance of cavitation erosion and abrasion (CEA) on the common properties of materials, four typical materials (WC coating, NiCr alloy coating, boron stainless steel and titanium) were used to do the experiments of CEA and cavitation erosion (CE), to do corrosive experiment, and to test their hardnesses. The experiments results indicated that all resistance to CEA and resistance to CE depend on the hardness and the corrosive resistance of materials. The high hardness is the first factor of good resistance to CEA, strong corrosive resistance is the second factor. Meanwhile, the strong corrosive resistance is the first factor of good resistance to CE, high hardness is the second factor.

Figures

图1

图2

图3

图4

图5

图6

图7

References

[ 1 ] HeathcockCJ, BallA .Cavitationerosionofcobalt basedstellitealloyscementedcarbidesandsufact treatedlowalloysteels[J].Wear, 1982:11~27

[ 2 ] FellerHG , KharraziY .Deformationanderosionoff.c.cmetalsandalloysundercavitationattack[J].Wear, 1984, (93) :249~260

[ 3 ] KarimiA , MartinJL .Cavitationerosionofmaterials[J].InterMaterialsReview, 1986, 31 (1) :1~25

[ 4 ] RickerbyDG , OkadaT .Incubation periodandcavitationerosionResistanceofsomeMetals[J].Wear, 1992, (156) :33~47

[ 5 ] VerdonC , KarimiA , MartinJ .AstudyofHVOFthermalsprayedtungstencarbidebasedcoating[J].MaterialsScienceandEngineering.1998, (A246) :11~24

[ 6 ] 陈文革, 谷臣清, 沈福三.钢的气蚀抗力与力学性能的相关性[J].水力发电学报, 1998, (2) :79~87 link1

[ 7 ] 陈文革, 谷臣清, 沈福三.钢的磨蚀抗力与力学性能的相关性[J].西安理工大学学报, 1998, (4) :422~426 link1

[ 8 ] WangBiao, WuBing, BellT .Studyofelectroplatingrareearthchromiumanditspropertiesandmicrostructure[A].InterconfonSurfaceEngineerings[C].NewcastleUK :EllisHorwoodLimited, 1990.676~686

[ 9 ] 王 飚, 王宇栋, 张自华.周期反相电镀稀土铬提高水轮机的抗空蚀磨损能力[J].中国腐蚀与防护学报.2003, (2) :24~30 link1

Related Research