Experimental Analysis of Glass Cutting by Laser Thermal Str ess
Project Management Research Institute, Southeast University, Nanjing, 210096
Next Previous
Abstract
When the output power of the CO2 laser machine reaches100W on average, the round focusing point can be formed on the surface of glass by the focusing light path. The laser energy of 10.6μm wavelength is absorbed fiercely by the15μm_thick glass layer on the surface, and the locol stress line distributing is formed. At the same time the quenching mouth is blowing the colder air onto the glass surface, quenching the thermal area quickly. The temperature of the glass surface is higher than the softening point, blowing colder air onto the surface forms the thermal stress concentrtion layer. The glass is disconnected along the cut which is made by mechanic means before cutting, and the crack is smooth. The best pace of the laser thermal stress cutting is 400 mm/s which is testified by the experiment.
Keywords
Figures
图 1
图 2
图 3
图 4
References
[ 1 ] 罗 福 ,孙承纬 ,杜祥琬 .1.6 Lm 连续激光照射下 K9玻璃板的应力松驰破坏[J] .强激光与粒子束 , 2001 ,13(1) :19 ~ 23
[ 2 ] 江 超 .KrF 准分子激光精密加工 K9 光学玻璃的实 验研究[J] .电加工与模具 ,2003 ,(3) :33 link1
[ 3 ] 晓 晨 .以激光切割玻璃[J] .激光与光电子学进展 , 1999 ,(8) :41
[ 4 ] 杜少军 ,陆启生 ,赵伊君 ,等 .激光窗口形状对应力 和光束位相影响的数值计算[J] .强激光与粒子束 , 2000 ,12(3) :273 ~ 276 link1
[ 5 ] 陈小伟 ,陈裕泽 ,余同希 ,等 .热力联合作用弹性薄 圆板的弯曲与屈曲[J] .强激光与粒子束 , 1998 , 10 (4) :531 ~ 536 link1
[ 6 ] Kim W S , Hector L G , Hetnarski R B . Thermoelastic stresses in a bonded layer due to repetitively pulsed laser radiation [J] .Acta Mechanica ,1997 ,125 :107 ~ 128 link1
[ 7 ] 孙承纬 ,赵剑衡 ,袁永华 ,等 .分束镜的非工作波段 激光作用失效机制[A] .激光的热和力学效应学术会 议论文集[C] .中国广西 ,2000 .1 ~ 7
[ 8 ] http ://www .antelaser .com [EB/OL]
[ 9 ] 龚 辉 ,王明利 .连续 CO2 激光对熔石英表面的增 强处理研究[J] .中国激光 ,1997 ,24(3) :256 ~ 257 link1
京公网安备 11010502051620号