Welding performance research of low cost hot rolled dual phase steel
1. Compact Strip Production Plant，Baotou Iron & Steel（Group）Co. Ltd.，Baotou，Neimenggu 014010，China;
2. The State Key Laboratory of Rolling and Automation，Northeastern University，Shenyang 110819，China
Next Previous
Abstract
The tensile properties，impact toughness and hardness of the welded joints of DP590 low-cost hot rolled dual phase steel using appropriate welding wire，flux and reasonable welding process was studied. The excellent softening resistance，cold bending formability and low hardening tendency of the test steels was shown. Experimental results showed that the DP590 low- cost hot rolled dual phase steel with good welding performance was suitable for welding car wheels and beams，etc.
Keywords
Figures
图1
图2
图3
图4
References
[ 1 ] 杨晓华. 热轧双相钢焊接性能研究[J]. 太原工业大学学报，1991 （22）：97-98. link1
[ 2 ] 阎 启. 热轧高强双相钢焊接性研究[J]. 焊接（生产应用），2008 （7）：50-52. link1
[ 3 ] 韩 强，陈 沅，麻永林，等. 热轧DP590双相钢焊接接头组织 的研究[J]. 焊接技术（试验与研究），2011（40）：13-15. link1
[ 4 ] 中华人民共和国国家质量监督检验检疫总局，中国国家标准化 管理委员会. GB/T 8110—2008 气体保护电弧焊用碳钢、低合 金钢焊丝[S]. 北京：中国标准出版社，2008.
[ 5 ] 李亚江. 高强钢的焊接[M]. 北京：冶金工业出版社，2010.
[ 6 ] 马鸣图，吴宝榕. 双相钢——物理和力学冶金[M]. 北京：冶金工 业出版社，1988.
[ 7 ] 李亚江. 焊接缺陷分析与对策]M]. 北京：化学工业出版社， 2011.
[ 8 ] Ohtani H，Okaguchi S，Fujishiro Y，et al. Morphology and properties of low carbon Bainite [J]. Metall Trans A，1990（21）：877- 881. link1
京公网安备 11010502051620号