A series of cathodes with MnO catalysts of metal fuel battery were prepared. The catalyst slurry was treated by ultrasonic dispersion under the ultrasonic time of 20 min, 40 min and 60 min. The cathodes were also dried with the temperature of 90°C, 120°C and 150°C. Besides, the microstructures of the cathodes and discharging performance were investigated. The results indicated that the ultrasonic time and drying temperature had a remarkable influence on the electric current densities, but had little effect on the open-circuit voltage. The effects of oxygen on the current density and voltage of cathode were also studied, and it was found that the method of blowing oxygen to cathode could increase the current density of the metal fuel battery.