Chloride ingress and macro-cell corrosion of steel in concrete made with recycled brick aggregate
1. Department of Civil and Environmental Engineering, Islamic University of Technology, Board Bazar, Gazipur 1704, Bangladesh;2. Department of Civil Engineering, University of Information Technology and Sciences, Baridhara, Dhaka 1202, Bangladesh;1. Department of Civil and Environmental Engineering, Islamic University of Technology, Board Bazar, Gazipur 1704, Bangladesh;1. Department of Civil and Environmental Engineering, Islamic University of Technology, Board Bazar, Gazipur 1704, Bangladesh;3. Bangladesh Road Research Laboratory, Roads and Highways Department, Mirpur, Dhaka 1216, Bangladesh
收稿日期:
2021-03-31
录用日期:
2022-01-21
发布日期:
2021-12-15
摘要
An investigation on chloride ingress and macro-cell corrosion of steel bars in concrete made with recycled brick aggregate (RBA) was carried out. As control cases, virgin brick aggregate (BA) and stone aggregate (SA) were also investigated. Both cylindrical and cracked prism specimens were studied for 16 different cases. The prism specimens were made with a segmented steel bar providing electrical connection from outside of the specimens to measure macro-cell corrosion current continuously under seawater splash exposure for a period of 30 d using a data logger. Cylindrical specimens were submerged in 3% NaCl solution at a temperature of 40°C to investigate chloride ingress in concrete made with RBA, BA, and SA after 120 and 180 d. Half-cell potential, corrosion area, and depths of corrosion were also investigated. The chloride ingress as well as corrosion of steel bars in concrete made with the different types of aggregate is ordered as RBA > BA > SA.