Hydrogenation of furfuryl alcohol to tetrahydrofurfuryl alcohol on NiB/SiO2 amorphous alloy catalyst

2007年第1卷第2期

大纲

摘要

关键词

《化学科学与工程前沿（英文）》 >> 2007年第1卷第2期 doi: 10.1007/s11705-007-0028-2

Hydrogenation of furfuryl alcohol to tetrahydrofurfuryl alcohol on NiB/SiO2 amorphous alloy catalyst

展示更多

Institute of New Catalytic Material Science, College of Chemistry, Nankai University, Tianjin 300071, China;

发布日期：2007-06-05

摘要

NiB/SiO amorphous alloy catalyst was prepared by power electroless plating method and characterized by induction coupled plasma (ICP), Brunauer Emmett Teller method (BET), transmission electron microscope (TEM) and X-ray diffraction (XRD) techniques. The catalytic performance of NiB/SiO was investigated for the hydrogenation of furfuryl alcohol (FA) to tetrahydrofurfuryl alcohol (THFA). The effects of operational conditions, such as reaction temperature, pressure, and stirring rate were carefully studied. The proper conditions were determined as the following: pressure 2.0 MPa, temperature 120?C and stirring rate 550 r/min. A typical result with FA conversion of 99% and THFA selectivity of 100% was obtained under such conditions, which was close to that over Raney Ni.

关键词

following ; Brunauer ; electroless ; temperature ; transmission

正文