Frontiers of Chemical Science and Engineering
>> 2021,
Volume 15,
Issue 3
doi:
10.1007/s11705-020-1981-2
RESEARCH ARTICLE
Efficient MgO-doped CaO sorbent pellets for high temperature CO
Key Laboratory for Green Chemical Technology (Ministry of Education), Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China
Received: 2020-10-22
Accepted: 2020-12-28
Available online: 2020-12-28
Next
Previous
Abstract
Novel MgO-doped CaO sorbent pellets were prepared by gel-casting and wet impregnation. The effect of Na and MgO on the structure and CO adsorption performance of CaO sorbent pellets was elucidated. MgO-doped CaO sorbent pellets with the diameter range of 0.5 1.5 mm exhibited an excellent capacity for CO adsorption and adsorption rate due to the homogeneous dispersion of MgO in the sorbent pellets and its effects on the physical structure of sorbents. The results show that MgO can effectively inhibit the sintering of CaO and retain the adsorption capacity of sorbents during multiple adsorption-desorption cycles. The presence of mesopores and macropores resulted in appreciable change of volume from CaO (16.7 cm ∙mol ) to CaCO (36.9 cm ∙mol ) over repeated operation cycles. Ca2Mg1 sorbent pellets exhibited favorable CO capture capacity (9.49 mmol∙g ), average adsorption rate (0.32 mmol∙g ∙min ) and conversion rate of CaO (74.83%) after 30 cycles.
京公网安备 11010502051620号