Original Position Statistic Distribution Analysis (OPA) Study on the Quality of Billet

Central Iron & Steel Research Institute, Beijing 100081, China

Received: 2003-06-23 Available online: 2003-10-20

Next Previous

Abstract

On the basis of analysis of tens of thousands of primary signals corresponding to original positions of sample systematically, the degree of porosity, the degree of homogeneity and inclusions of billets can be quantitatively determined. The degree of porosity and the maximum degree of segregation for different billets were calculated accurately in the present paper. The weight ratio of carbon content at each original position of billet was suggested to express the degree of homogeneity of billets. Correspondingly, two models-the total weight ratio of carbon contents within the permissive content range (C0±R) and the confidence extension ratio of median value (K) at 95 % of confidence limit of weight ratio, were provided for practical billet samples analysis. This analysis technique was characterized by the primary, original and statistical nature of measured information, thus the quantitative statistic distribution analysis of chemical elements and their states in larger scale was realized. The quality differences among the billet samples were explained reasonably by above method. Thus, this technique can be used to judge the quality of billet samples.

Figures

图1

图2

图3

图4

图5

图6

图7

图8

图9

图10

References

[ 1 ] 王海舟.原位统计分布分析———材料研究及质量判据的新技术[J].中国科学 (B辑) , 2002, 32 (6) :481~484 link1

[ 2 ] 王海舟.21世纪冶金分析的若干问题[J].钢铁, 2000, 35 (1) :73~78 link1

[ 3 ] 王海舟.面向新世纪的冶金材料分析[J].理化检验 (化学分册) , 2001, 37 (1) :1~4;2001, 37 (2) :49~52 link1

[ 4 ] 王海舟.金属原位分析系统[J].中国冶金, 2002, (6) :20~22 link1

[ 5 ] 陈吉文, 王海舟, 杨志军, 等.火花数字光谱解析技术[A].第十届全国光谱分析学术年会论文集[C].北京:中国金属学会理化检验委员会, 全国冶金分析信息网, 2000.B119~B122

[ 6 ] 杨志军, 王海舟.火花光谱原位分析技术对连铸方坯质量分析的应用研究[J].钢铁, 2002, 37 (增刊) :189~193

[ 7 ] 杨志军, 王海舟.用原位分析方法研究连铸板坯的偏析和夹杂火花光谱原位分析技术对连铸方坯质量分析的应用研究[J].钢铁, 2003, 38 (3) :61~63

[ 8 ] 高宏斌, 贾云海, 王海舟.钢中不同状态铝的光谱行为研究[A].第十届全国光谱分析学术年会论文集[C].北京:中国金属学会理化检验委员会, 全国冶金分析信息网, 2000.B1~B5

Related Research