Damage Assessment Techniques for Pitting Corroded Structures
1. Department of Physics & Electrical Information Engineering, Ningxia Unversity, Yinchuan 750021, China;
2. Department of Aircraft Engineering, Northwestern Polytechnical University, Xi'an 710072, China
Next Previous
Abstract
The finite element method and local stress and strain method were used to obtain the crack initiation life under fatigue load of each pit. After getting the life of crack initiation, the propagation life of initiation crack under pits bottom and the equivalent initial surface crack size were calculated through reverse integration of the Paris fatigue crack growth law and solving the non-linear equation using fracture model. Finally the nonlinear relation was set up between sizes of pits and equivalent initial surface crack by neural network.
Keywords
corrosion pit ; finite element method ; local stress and strain ; Monte Carlo method ; neural network
Figures
图 1
图 2
图 3
References
[ 1 ] ASME.ASME boiler and pressure vessel design code, SectionⅪ [ S ] .Philadelphia: American Society of Mechanical Engineers, 1992
[ 2 ] 尚德广,王德俊,等.疲劳裂纹萌生尺寸的定义及其确定方法[J].机械强度,1996,18(2):59~62 link1
[ 3 ] 赵少汴.局部应力应变法及其设计数据[J].机械设计,2000,(2):1~4 link1
[ 4 ] Leek T H, Howard I C.An examination of methods of assessing interacting surface cracks by comparison with experimental data [ J] .Int J Pres & Piping, 1996 , 68 : 181 ~201 link1
[ 5 ] Newman J C Jr, Raju I S.An empirical stress intensity factor equation for the surface crack [ J] .Engng Fracture Mech, 1981 , ( 15 ) :185 ~92 link1
京公网安备 11010502051620号