Low temperature synthesis of visible light responsive rutile TiO

ARC Centre of Excellence for Functional Nanomaterials, School of Chemical Engineering and AIBN, the University of Queensland, Brisbane 4072, Australia

发布日期： 2012-03-05
HTML7 PDF 2 收藏 0

下一篇 上一篇

摘要

A nano-structured TiO with rutile phase was synthesized by using the hydrothermal method from a titanium carbide (TiC) nano-powder precursor at low temperature to produce a stable visible light responsive photocatalyst. The rutile phase was formed at temperature as low as 100°C, and both synthesis time and temperature affected its formation. The rutile particles showed a faceted nano-rod structure, and were tested for absorption and photo-degradation ability under visible light. Particles with shorter synthesis times showed higher visible light absorption and corresponding photo-degradation ability, while those synthesized at lower temperatures had lower, but still evident, degradation ability under visible light.

相关研究