Division of Functional Materials Research, Central Iron and Steel Research Institute, Beijing 100081, China
Next Previous
Abstract
In this paper, high performance of anisotropic de-upset nanoscale Nd-Fe-B magnets is obtained: intrinsic coercivity Hcj=1 157 kA/m, remanence Br=1.465 T and maximum energy product (BH)max=426 kJ/m3. The fabrication procedure dependence, deformation mechanism and magnetic domains of these materials are discussed. It is found that the strain activation energy of the die-upset Nd-Fe-B magnets is about 380 kJ/mol based on the Arrhenius Model. The interaction domains are the typical characteristics of the magnetic structures of the magnets. And these domains play an important role in the coercivity mechanism and the corresponding maximum application temperature for the die-upset Nd-Fe-B magnets.
Figures
图1
图2
图3
图4
图5
图6
图7
图8
图9
图10
图11
图12
图13
图14
References
[ 1 ] Lee R W.Hot-pressed neodymium-iron-boron magnets [ J] .Appl Phys Lett, 1985 ,46 ( 8 ) :790 -791. link1
[ 2 ] Mishra R K, Brewer E G, Lee R W.Grain -growth and align- ment in hot deformed Nd -Fe -B magnets [ J ] .J Appl Phys, 1988 ,63 ( 8 ) :3528 -3530. link1
[ 3 ] Fuerst C D, Brewer E G.Enhanced coercivities in die-upset Nd - Fe -B magnets with diffusion-alloyed additives ( Zn, Cu, Ni ) [ J] .Appl Phys lett, 1990 , 56 ( 22 ) :2252 -2254. link1
[ 4 ] Saito T, Fujita M, Kuji T, et al.The development of high per- formance Nd -Fe -Co -Ga -B die-upset magnets [ J] .J Appl Phys,1998 ,83 ( 11 ) :6390 -6392. link1
[ 5 ] 李 卫,祝景汉,蒋 龙,等.辐向取向钕铁硼永磁环及其制造 方法[ P] .中国:ZL 88103837.7 ,1991.
[ 6 ] 李 卫,李传健,李岫梅,等.多织构整体烧结成型稀土永磁环 及其制造方法[ P] .中国:ZL 02124002.7 ,2004.
[ 7 ] Li Anhua, Dong Shengzhi, Li Wei.A study of the anisotropy of mechanical properties and fracture behaviour in sintered Sm2 Co17 permanent magnetic materials [ J] .Acta Physica Sinica, 2002 ,51 ( 10 ) :2320 - 2324.
[ 8 ] 刘兴民.先进稀土永磁多极环制备技术的研究[D].北京:钢铁研究总院,2007.
[ 9 ] 张鑫,阎俊萍,孙昊.铸造-热变形Nd-Fe-B永磁合金显微组织及性能的研究[J].包头钢铁学院学报,2004,23(3):250-253. link1
[10] 吴承义,张丽英,柴立民,等.Nd-Fe-B快淬粉末热压工艺研究[J].新技术新工艺,1998(3):12-13.
[11] Ragg O M, Arris I R.Hot pressing Nd -Fe -B HDDR powders [ J] .IEEE Transactions On Magnetics, 1996 , 32 ( 5 ) : 4395 - 4397. link1
[12] Grünberger W, Hinz D, Kirchner A, et al.Hot deformation of nanoerystalline Nd -Fe -B alloys [ J] .J Alloy Compd, 1997 , 257 ( 1 -2 ) :293 -301.
[13] Li L, Graham C D.The origin of crystallographic texture pro- duced during hot deformation in rapidly-quenched Nd -Fe -B permanent magnets [ J] .IEEE Transactions on Magnetics,1998 , 28 ( 5 ) :2130 -2132. link1
[14] 赵睿.纳米晶Nd-Fe-B磁体的热变形机制及磁性能研究[D].北京:钢铁研究总院,2011.
[15] 赵睿,王会杰,李家杰,等.热模压Nd-Fe-B磁体变形过程及其模拟研究[J].功能材料,2011,42(3):512-515. link1
[16] Leonowicz M, Davies H A.Effect of Nd content on induced ani- sotropy in hot deformed Fe -Nd -B magnets [ J] .Materials Let- ters, 1994 ,19 :275 -279. link1
[17] Yoshida Y, Kasai Y, Watanabe T, et al.Hot workability of melt-spun Nd -Fe -Co -B magnets [ J] .J Appl Phys, 1991 , 69 ( 8 ) :5841 -5843. link1
[18] Dariel M P.Handbook on the Physics and Chemistry of Rare Earths [ M] .New York: North -Holland, 1978 :847 -875.
[19] Zhu M G, Wang H J, Li W, et al.Study on preferred orientation in Nd -Fe -B cast strip [ J] .Iron and Steel Research, 2006 ,13 ( suppl.1 ) :119 -121. link1
[20] Kwon W H, Yu J H.Texture studies on die-upset Nd-lean Nd - Fe-( Cu) -Ga-B alloy [ J] .IEEE Trans Magn, 2009 , 45 ( 10 ) : 4435 -4438. link1
[21] Craik D J, Isaac E D.Magnetic interaction domains [ J] .Proc Phys Soc,1960 ,76 :160 -162.
[22] Fang Y K, Chang H W, Guo Z H, et al.Magnetic microstruc- tures of phase-separated SmCo 2 : 17 -type sintered magnets [ J] .J Alloy Compds, 2008 ,462 :376 -380. link1
京公网安备 11010502051620号