Study of properties and the preparation of composite of wheat straw and HDPE/PP
Key Laboratory of Bio- based Material Science and Technology，Ministry of Education，Northeast Forestry University，Harbin 150040，China
Next Previous
Abstract
The paper is mixing the raw materials of wheat straw as enhanceosome and highdensity polyethylene/pohyprpylene (HDPE/PP) of thermoplastic to produced wood-plastic composite by adopting extrusion way and researching effect about the content of HDPE and PP on the properties of composite. Under a certain conditions，the high-speed mixer mixed the compound of wheat straw powder and thermoplastics and other auxiliaries，and then the compound were melting prilling by twin-screw extruder followed and molding by the single screw extruder.The mechanical properties of composite of wheat straw and thermoplastic were measured .The results indicated that adding a small amount of wheat straw powder caused the reduction of mechanical properties of wood plastic composite，the mechanical properties of wood plastic composite increased with increasing wheat straw powder content，mechanical properties decreased when the content of wheat straw was more than a certain percentage，especially，the impact property decreased obviously；the test indicated that the mechanical properties of HDPE were higher than PP.
Keywords
wheat straw powder ; HDPE ; PP ; composite materials ; performance studies
Figures
图1
图2
图3
图4
References
[ 1 ] 李 坚.生物质复合材料[M]. 北京：科学出版社，2008.
[ 2 ] 许 民. 生物质——塑料复合工学[M]. 北京：科学出版社，2006.
[ 3 ] 严涛海.亚麻热塑性增强复合材料成型工艺及性能研究[D].上 海：东华大学，2009. link1
[ 4 ] Lunt J. Large-scale production，properties and commercial applications of polylactic acid polymers [J]. Polymer Degradation and Stability，1997：145-152. link1
[ 5 ] 郭文静，鲍甫成，王 正. 天然植物纤维可生物降解塑料复合材 料一种完全环境友好的新型生物质复合材料[C]//全国生物质 材料暨环保型人造板新技术发展研讨会论文集. 山东：中国林 学会木材工业分会，2006：95-98.
[ 6 ] Mohanty A K，Mistra M，Drzal L T.Sustainable bio-composites from renewable resources：Opportunities and challenges in the green materials world[J]. Polymer Degradation and Stability， 2002：19-26. link1
京公网安备 11010502051620号