2014, Volume 16, Issue 2
Strategic Study of CAE >> 2014, Volume 16, Issue 2
Development and formability analysis of TRIP seamless steel tube
1.Modern Design and Analysis Institute，Northeastern University，Shenyang 110819，China；
2. School of Mechanical Engineering and Automation，Northeastern University，Shenyang 100819，China;
3. State Key Laboratory of Rolling and Automation，Northeastern University，Shenyang 110819，China
Next Previous
Abstract
In the present study，the production technology of transformation induced plasticity（TRIP）steel was firstly introduced in the steel tube manufacture field. The TRIP steel tubes with a microstructure of ferrite，bainite，retained austenite and a little martensite were successfully fabricated with both of the two-stage heat treatment technique and continuous heat treatment technique using a cold drawn steel tube. The ring tensile test and cold bending process were carried out to study the formability of the newly developed TRIP seamless steel tube. The results showed that the TRIP seamless steel tubes have a good cold formability，and they are available to be used in the tube hydroforming process. In addition，the equipment of continuous heat treatment developed in the current study can be used to produce TRIP steel tube and it may serve as an important reference for the industrial production of TRIP steel tube.
Keywords
TRIP steel ; heat treatment ; formability ; steel tube ; microstructure
Figures
图1
图2
图3
图4
图5
图6
图7
图8
References
[ 1 ] Mildenberger Udo，Khare Anshuman. Planning for an environment-friendly car [J]. Technovation，2000，20（4）：205-214.
[ 2 ] Kocë Muammer，Altan Taylan. An overall review of the tube hydroforming（THF）technology [J]. Journal of Materials Processing Technology，2001，108（3）：384-393.
[ 3 ] Morphy G. Tubular hydroforming：Ability and exibility of pressure sequencing [C]// Proceedings of the Tube and Pipe Association Conference on Hydroforming. Chicago，USA，1997.
[ 4 ] 关小军，周家娟，王作成. 一种新型汽车用钢——相变诱发塑 性钢[J]. 特殊钢，2000，21（2）：27-30.
[ 5 ] Li Yuxuan，Lin Zhongqin，Jiang Aiqin，et al. Use of high strength steel sheet for lightweight and crashworthy car body [J]. Materials & Design，2003，24（3）：177-182.
[ 6 ] American Iron and Steel Institute. Ultralight steel auto body final report [R]. Washington DC：American Iron and Steel Institute， 1998.
[ 7 ] Masumura Osamu，Sakuma Yasuharu，Takechi Hiroshi. Enhancement of elongation by retained austenite in intercritical annealed 0.4C- 1.5Si- 0.8Mn steel [J]. Transactions of the Iron and Steel Institute of Japan，1987，27（4）：570-579. link1
[ 8 ] Matsumura O，Sakuma Y，Takechi H. TRIP and its kinetic aspects in austempered 0.4C-1.5Si-0.8Mn Steel [J]. Scripta Metallurgica，1987，21：1301-1306. link1
[ 9 ] Chen H C，Era H，Shimizu M. Effect of phosphorus on the formation of retained austenite and mechanical properties in Sicontaining low carbon steel sheet [J]. Metallurgical and Materials Transactions A，1989，20（3）：437-445. link1
[10] Sakuma Yasuharu，Matlock David K，Krauss George. Mechanical behavior of an intercritically annealed and isothermally transformed low C alloy steel with ferrite- bainite-austenite microstructures [J]. Journal of Heat Treating，1990，8（2）：109- 120. link1
[11] Sugitomo Koh-ichi，Misu Masahiro，Kobayashi Mitsuyuki，et al. Effects of second phase morphology on retained austenite morphology and tensile properties in a TRIP- aided dual- phase steel sheet [J]. Iron and Steel Institute of Japan，1993，33（7）： 775-782. link1
[12] Sakuma Yasuharu，Matsumura Osamu，Takechi Hiroshi. Mechanical properties and retained austenite in intercritically heattreated bainite-transformed steel and their variation with Si and Mn additions [J]. Metallurgical and Materials Transactions A， 1991，22（2）：489-498. link1
[13] Sakuma Y，Matlock D K，Krauss G. Intercritically annealed and isothermally transformed 0.15 pct steels containing l.2 pct Si-1.5 pct Mn and 4 pct Ni：Part 1 [J]. Metallurgical and Materials Transactions A，1992，23（4）：1221-1232. link1
[14] Pereloma E V，Timokhina I B，Hodgson P D. Transfomation behaviour in thermomechanically processed C-Mn-Si TRIP steels with and without Nb [J]. Materials Science and Engineering：A，1999，273-275：448-452. link1
[15] Zhang Z C，Manabe K，Zhu F X，et al. Determination of circumferential mechanical properties of TRIP steel tube by ring tensile test [J]. Steel Research International，2010，81（9）： 568-571.
[16] De Cock T，Ferrer J P，Capdevila C，et al. Austenite retention in low Al/Si multiphase steels [J]. Scripta Materialia，2006，55 （5）：441-443. link1
[17] Emadoddin E，Akbarzadeh A，Daneshi G. Effect of intercritical annealing on retained austenite characterization in textured TRIP-assisted steel sheet [J]. Materials Characterization，2006， 57（4/5）：408-413. link1
[18] Timokhina I B，Hodgson P D，Pereloma E V. Effect of microstructure on the stability of retained austenite in transformationinduced-plasticity steels [J]. Metallurgical and Materials Transactions A，2004，35（8）：2331-2341. link1
京公网安备 11010502051620号