Preparation of superhydrophobic wood by an in situ sol-gel process
College of Materials Science and Engineering，Central South University of Forestry and Technology，Changsha 410004，China
Next Previous
Abstract
Superhydrophobic wood was prepared by an in situ sol-gel process. The wood surface was covered by a thin layer of nanostructured superhydrophobic film，and the contact angle of water droplet on the wood surface reached 150.6°. The phase composition，surface morphology and chemical groups of the superhydrophobic wood sample were observed by X-ray diffraction (XRD)，scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR)，respectively. The results revealed that the rough surface with nanoscale projections combined with hydrophobic vinyl groups on the surface contribute to the superhydrophobic property of the wood surface.
Keywords
wood ; superhydrophobic ; sol-gel ; nanoscale
Figures
图1
图2
图3
图4
图5
References
[ 1 ] Hsieh Chien- Te，Chang Bi- Sheng，Lin Jia- Yi. Improvement of water and oil repellency on wood substrates by using fluorinated silica nanocoating [J]. Applied Surface Science，2011，257(18)： 7997-8002. link1
[ 2 ] Roach Paul，Shirtcliffe Neil J，Newton Michael I. Progess in superhydrophobic surface development [J]. Soft Matter，2008，4 (2)：224-240. link1
[ 3 ] 赵 宁，卢晓英，张晓艳，等. 超疏水表面的研究进展[J]. 化学 进展，2007，19(6)：860-871. link1
[ 4 ] Wang Chengyu，Piao Cheng，Lucas Cran. Synthesis and characterization of superhydrophobic wood surfaces [J]. Journal of Applied Polymer Science，2011，119(3)：1667-1672.
[ 5 ] Liu Changyu，Wang Shuliang，Shi Junyou，et al. Fabrication of superhydrophobic wood surfaces via a solution- immersion process [J]. Applied Surface Science，2011，258(2)：761-765. link1
[ 6 ] Sun Qingfeng，Lu Yun，Liu Yixing. Growth of hydrophobic TiO2 on wood surface using a hydrothermal method [J]. Journal of Materials Science，2011，46(24)：7706-7712. link1
[ 7 ] Hong Jung-Kyun，Kim Hong-Ryul，Park Hyung-Ho. The effect of sol viscosity on the sol- gel derived low density SiO2 xerogel film for intermetal dielectric application [J]. Thin Solid Films， 1998，332(1/2)：449-454. link1
[ 8 ] Parrill T M. Transmission infrared study of acid-catalyzed sol-gel silica coatings during room ambient drying [J]. Journal of Materials Research，1992，7(8)：2230-2239. link1
[ 9 ] Fan Youhua，Li Changzhu，Chen Zejun，et al. Study on fabrication of the superhydrophobic sol-gel films based on copper wafer and its anti- corrosive properties [J]. Applied Surface Science， 2012，258(17)：6531-6536. link1
[10] Liang Jin，Hu Yunchu，Fan Youhua，et al. Formation of superhydrophobic cerium oxide surfaces on aluminum substrate and its corrosion resistance properties [J]. Surface and Interface Analysis，2013，45(8)：1211-1216. link1
京公网安备 11010502051620号